The Standard Enthalpies of Formation of Some Binary Intermetallic Compounds of Lanthanide – Iron Systems by High Temperature Direct Synthesis Calorimetry

Speaker

Dr. Susan Meschel

University of Chicago

时间:10月23日 (星期二)下午14:30

地点:2号楼607会议室

联系人:张文清研究员

Abstract

The standard enthalpies of formation of intermetallic compounds of some Lanthanide-iron systems have been measured by high temperature direct synthesis calorimetry at 13732K. The following results in kJ/mole of atoms are reported: Ce2Fe17(-1.6 2.8); Pr2Fe17(-0.23.0); Nd2Fe17(-3.02.7); Sm2Fe17(-3.13.2 ); GdFe2(-2.43.0); HoFe2(-2.63.3); ErFe2(-1.93.0); TmFe2(-2.22.8); LuFe2(-3.6 3.1).

The standard enthalpies of formation of some binary and ternary shape memory alloys have also been measured. These are: Terfenol-D(-1.53.1), Samfenol(-13.63.1), Galfenol(-10.42.8).The values are compared with predicted values of the semi empirical model of Miedema and Coworkers and with predictions by ab initio calculations. We will present a systematic picture of how the enthalpies of formation may be related to the atomic number of the Lanthanide element. We will also compare the thermochemical behavior of LA-Ni and the LA-Fe alloys.

 
 